Solid Wire Electrode BA-S1CrMo2 for Submerged Arc Welding

Classification:
EN ISO 24598-A (EN 12070): S S CrMo2
SFA 5.23 / AWS A5.23: EB3(R)

Main Application

CrMo-alloyed low impurity wire electrode (suitability for step-cooling) for submerged arc welding of heat-resistant steels in boiler and pressure vessel construction as well as pipe manufacture.

Typical analysis and chemical composition acc. to EN ISO 24598-A and AWS A5.23

Wire electrode C Si Mn Mo Ni Cr P S Others
Typical analysis BA-S1CrMo2 0.10 0.18 0.64 1.02 0.02 2.4 0.008 0.007 Cu total
0.09
S S CrMo2 acc. to ISO 24598-A 0.08 - 0.15 0.05 - 0.25 0.30 - 0.70 0.90 - 1.15 0.3 2.2 - 2.8 0.020 0.020 V 0.03
Nb 0.01
Cu 0.03
EB3 acc. to AWS A5.23 0.05 - 0.15 0.05 - 0.30 0.40 - 0.80 0.90 - 1.10 - 2.25 - 3.00 0.025 0.025 Cu 0.35
EB3R: As / Sn / Sb 0.005 - - - - - - 0.010 0.010 Cu 0.15

Base Materials

Heat-resistant steels acc. to EN 10028 and ASTM: 10CrMo9-10 / A182-F22 / A387 Gr. 22
suitable fluxes BF 10 and BF 16

Flux type suitability is strongly dependent on its application. In combination with the wire electrode the most suitable flux should match the requirements of the plate material as closely as possible under the existing welding conditions. Further information can be obtained from the technical flux data sheets.

Package Forms

Coils, spools, drums and spiders as standard package forms for SAW-wire electrodes, different package forms on request.

Diameter

2.0 – 5.0 mm; Sizes and tolerances acc. to ISO 544 and AWS A5.23.

Wire Electrode Surface

Copper-coated, smooth finish free from surface defects and foreign matter.

 